New Water-Ethylene Glycol Lubricants with Stearate Ionic Liquid Crystal Additive
Avilés, María-Dolores; Sánchez-Rodríguez, Cristian; Pamies, Ramon; Bermúdez, María-Dolores; Carrión-Vilches, Francisco-José; Sanfèlix, Susana García; Kjøniksen, Anna-Lena
Peer reviewed, Journal article
Published version
![Thumbnail](/hiof-xmlui/bitstream/handle/11250/3049275/lubricants-10-00241-v2.pdf.jpg?sequence=6&isAllowed=y)
View/ Open
Date
2022Metadata
Show full item recordCollections
Abstract
The main purpose of the present study is to improve the tribological performance of aqueous lubricants with the use of ecofriendly, fatty acid-derived additives. The protic ionic liquid crystal bis(2-hydroxyethyl)ammonium stearate (DES) has been added to 50:50 water+ethylene glycol (W–EG) to obtain (W–EG)+0.5%DES; (W–EG)+1%DES and (W–EG)+2%DES emulsions. The new lubricants have been studied in sapphire-AISI (American Iron and Steel Institute) 316L stainless-steel pin-on-disk sliding contacts. The addition of DES reduces the friction coefficient by up to 76% and wear rate by up to 80%, with respect to (W–EG). The best performance is found for the emulsions with the lower proportion of DES (0.5 and 1 wt.%). These results have been related to viscosity and turbidity values. Wear mechanisms have been studied by Scanning Electron Microscopy/Energy Dispersive X-ray Spectroscopy (SEM/EDX) and by Raman microscopy. While W–EG shows a severe abrasive mechanism, no abrasion marks are present inside the wear track after lubrication with (W–EG)+0.5%DES, the emulsion with the lowest wear rate. After lubrication with W–EG, an increase in oxygen content is observed inside the wear track, as determined by EDX and confirmed by Raman microscopy, which shows the presence of iron oxides. The addition of DES reduces these oxidation processes.